The Dispersion of Nanometer SIC on Electro Less Ni-P-Nano SIC Composite Plating
Hong Wang and Yubao Cao
Corresponding Author: Hong Wang
Submitted: July 27, 2012
Accepted: September 17, 2012
Published: May 01, 2013 |
Abstract:
|
In this study, we study the effects of the concentration of Sic using the orthogonal test method, the speed of mixing, the temperature and the surfactants on depositing rate and micro-hardness and obtain the optimized technological scheme and fine Ni-P-SIC composite coating. The results showed that using citric acid-acetic acid as complexing agents can obtain high speed of depositing and homogeneous coating with Sic well-distributed. Among the technological parameters, the effects of temperature on depositing rate are biggest and the surfactants are next; the effects of the concentration of Sic particles on micro-hardness are biggest and the surfactants are next. Give consideration to depositing rate and stability of the liquid, the temperature should be controlled at 82±2°C, the concentration of Sic particles and surfactants should be controlled in 4 g/L and 60 mg/L. The influence to micro-hardness value of coating with ultrasonic disperser craft also is studied.
Key words: Depositing rate, disperser, electro less composite plating, micro-hardness, microstructure, nanometer sic, speed of mixing ultrasonic, surfactant
|
Abstract
|
PDF
|
HTML |
|
Cite this Reference:
Hong Wang and Yubao Cao, . The Dispersion of Nanometer SIC on Electro Less Ni-P-Nano SIC Composite Plating. Research Journal of Applied Sciences, Engineering and Technology, (17): 4291-4294.
|
|
|
|
|
ISSN (Online): 2040-7467
ISSN (Print): 2040-7459 |
|
Information |
|
|
|
Sales & Services |
|
|
|