Nickel Based Coatings Containing TiN Nanoparticles Prepared by Ultrasonic-Electrodeposition Technology

Yong Wang, Fafeng Xia, Chao Liu and Hongyan Yin
Corresponding Author:  Fafeng Xia 

Key words:  Nickel, Coating, TiN, Ultrasonic-electrodeposition, , ,
Vol. 6 , (10): 1857-1861
Submitted Accepted Published
November 19, 2012 January 11, 2013 July 20, 2013

In order to enhance the surface properties of steel substrates, nano Ni-TiN composite coatings were prepared using ultrasonic-electrodeposition technology in this study. The effects of ultrasonic on composite coatings were studied. The X-Ray Diffraction (XRD) study had been utilized to detect the crystalline and amorphous characteristics of Ni-TiN composite coatings. The surface morphology and metallurgical structure of composite coatings were observed with Scanning Electron Microscope (SEM) and High Respective Transmission Electron Microscope (HRTEM). Finally the corrosion resistance was tested. The results show that the ultrasonic has greatly effects on TiN nanoparticles in composite coatings. And the introduction of ultrasonic and TiN particles cause the nickel grains to become fine. The average grain diameter of TiN particles is 30 nm. The Ni grain is measured approximately 60 nm. The test of corrosion resistance shows the nano Ni-TiN composite coating is proved with good corrosion resistance. The corrosion rate of 45 steel is about 5 times than that of Ni-TiN composite coating and the corrosion rate of Ni coating is above thrice than that of Ni-TiN composite coating.
Abstract PDF HTML
  Cite this Reference:
Yong Wang, Fafeng Xia, Chao Liu and Hongyan Yin , 2013. Nickel Based Coatings Containing TiN Nanoparticles Prepared by Ultrasonic-Electrodeposition Technology.  Research Journal of Applied Sciences, Engineering and Technology, 6(10): 1857-1861.
    Advertise with us
ISSN (Online):  2040-7467
ISSN (Print):   2040-7459
Submit Manuscript
   Current Information
   Sales & Services
   Contact Information
  Executive Managing Editor
  Email: admin@maxwellsci.com
  Publishing Editor
  Email: support@maxwellsci.com
  Account Manager
  Email: faisalm@maxwellsci.com
  Journal Editor
  Email: admin@maxwellsci.com
  Press Department
  Email: press@maxwellsci.com
Home  |  Contact us  |  About us  |  Privacy Policy
Copyright © 2009. MAXWELL Science Publication, a division of MAXWELLl Scientific Organization. All rights reserved